AgeSin® AP-L3170D is primarily formulated as a titanium acetylacetonate chelate, which remains stable at room temperature. During the application process, as solvents evaporate, the titanate can undergo cross-linking reactions with active groups (such as -OH, -COOH, -NH₂, -CONH₂, -SH) present on the substrate and within the ink or coating binder. This creates bridging bonds, increasing molecular weight and consequently enhancing properties like heat resistance, chemical resistance, water resistance, and drying performance. Ultimately, the bridging action of the titanate between the resin and the substrate improves the adhesion of inks and coatings,can replace Tyzor AA-75.
AgeSin® AP-L3170D
(溶剂-based | Titanium Chelate | Enhances Adhesion & Durability)
Equivalent alternative: Tyzor AA-75
组成 | titanium acetylacetonate complex |
外观 | Light yellow to light red transparent liquid |
Titanium Content | 9 - 10% |
Refractive Index (nD | 1.481 |
密度 (25°C) | 0.990 g/cm³ |
粘度 (25°C) | 6 mPa·s |
The above properties represent typical results and are not specifications. Refer to the specific COA for certified values.
溶剂-based
Enhances adhesion of inks and coatings to substrates (pre-treated plastics, aluminum foil, metals, glass).
Improves scratch resistance, water resistance, solvent resistance, and boil resistance of inks and coatings.
Increases drying speed, surface gloss, and pigment dispersibility in inks and coatings.
Substrate Pretreatment: Substrates (plastics, aluminum foil, metals, glass) typically require pretreatment (e.g., corona discharge, flame, or chemical treatment) to generate active groups like -OH or -COOH.
Resin Compatibility: Compatible with resins containing active groups (e.g., -OH, -COOH, -NH₂), such as PA, NC, PU, PVB, CAB, CAP, EVA.
Recommended Dosage: 0.5 - 3% (based on resin solids content).
Addition Method: It is recommended to add in the final stage of ink or coating manufacture at temperatures below 40°C. Ensure substrates are pretreated with a surface tension above 36-38 dynes/cm.
Post-Processing: After printing, inks should be cured at 60°C for 1 minute to facilitate the reaction between the titanate and the substrate.
Interaction with Antioxidants: Phenolic antioxidants can interact with titanium chelates, potentially causing color darkening. To avoid this issue in white inks, transparent inks, or light-colored topcoats, the use of aluminum chelates is recommended.
Storage Consideration: AgeSin® AP-L3170D is a strong chelating agent and can easily form chelates with metals. Therefore, storage in plastic containers is recommended.
● 25 公斤/桶, 200 公斤/桶
Store in a cool, ventilated area, away from heat and open flames.
Keep containers tightly sealed.
Shelf Life: 12 months unopened. Product exceeding the shelf life may be used after re-inspection.
Always reseal containers immediately after partial use.