AGESIN® Polyester modified polysiloxane copolymer solution
Product Number: AgeSin® LA-D511N
Equivalent alternatives: BYK-310, Elementis Levaslip 872 (D511N has lower surface tension and better slip)
| Composition | Polyester modified polysiloxane copolymer solution |
| Appearance | Transparent to slight yellowish liquid |
| Solvent | 二甲苯 |
| Density | 0.86-0.90 g/ml (25±1)℃ |
| Viscosity | 5-25s(Tu-4 viscometer)(25±0.2)℃ |
| Solid content | 13±3% (105℃ 3h) |
This data sheet is intended to give typical results, not standard.Subject to COA.
● Solvent-based
● Compared with ordinary polyester modified silicone, it can strongly reduce the surface tension of solvent-based coating systems and effectively prevent shrinkage cavities.
● Compared with polyether modified silicone, it is unstable in foaming and has excellent defoaming performance, which can effectively prevent the generation of “dark foam” on the surface of polyurethane glossy topcoat.
● Reduce the friction coefficient of the paint film surface, increase the slippery performance, and improve the anti-scratch ability.
● Improve gloss.
● Suitable for high-temperature baking paint system, good recoatability, does not affect the adhesion between layers.
Pre-diluted with the solvent of the coating system and added for easy mixing, post-addition is possible.
Suggest addition:
Addition to total formulation 0.1-0.5%
Transparency in varnish : 3
Defoaming : 4
Dynamic surface tension : 4
Static surface tension : 5
Slippery : 5
Anti-orange peel ability : 2
0=unavailable 5=very effective
● 25KG / 180KG
Being kept in dry, clean warehouse with well ventilation.
Avoid exposing to light and heating.