SINOMER UVP4299X-3D - 3D Printing Resin for Investment Casting

Sinomer® UVP4299X-3D

3D printing resin, investment casting resin, polyestser acrylate, Sartomer N3D-C179 alternative

SINOMER® UVP4299X-3D is a polyester acrylate resin with high-hardness, low-yellowing,the curing coating is volatile at high temperature,can be used in 3D printing and investment casting,as an alternative to Sartomer N3D-C179.

SINOMER® UVP4299X-3D
(Polyester Acrylate Resin for 3D Printing)

General Information:

技术指标 :

检验项目 (Item)	指标要求 (Specification)
外观 (Appearance)	澄清透明液体
色度 (APHA)	≤ 50
Viscosity (cps, 25°C)	90–180
Acid Value (mgKOH/g)	≤ 2.0
Specific Gravity (g/cm³)	1.10 ± 0.02
Refractive Index (25°C)	1.500 ± 0.005
Solid Content (%)	100

Features & Application :

High cured hardness
Low yellowing tendency
Suitable for high-temperature volatilization after curing
Designed as a direct alternative to Sartomer N3D-C179
Used for 3D printing casting patterns.

Curing Characteristics :

LED UV is the primary curing source for current UV printers.
Compatible with LCD printer systems. Recommended exposure: 4 s at 100W for optimal results.

Processing Recommendations :

1. Design & 3D printing
2. Investment casting
3. Clean burnout – Temperature ramp to 600–800°C, process duration 2–3 hours
4. Cooling & dissolving
5. Finished product

Post-Processing Equipment Recommended :

Ultrasonic cleaning pool (to remove residual resin)
Post-curing oven (for additional light curing to achieve desired properties)

Packaging & Storage :

Packaging: 25kg or 200kg/drum

Storage:

存放在干燥、阴凉、通风良好的库房内。

避免受光照和高温加热。

运输过程中做好防漏、防雨与防暴晒保护。

我们能帮您什么？

我们提供多种选择，帮助您找到适合您应用的产品。

Sinomer® UVU 62001SP-3D

urethane methacrylate, UV oligomer, Sartomer CN1970 alternative, dental model resin

SINOMER® UVU62001SP-3D is an aliphatic urethane methacrylate oligomer manufactured for 3D printing dental models, high-performance coatings and adhesives.

产品描述 :

Urethane Methacrylate
Viscosity (25℃) :

5,500 – 9,500mPa·s
Functionality :

2
Color (fe/co) :

≤100#
包装规格 :

20kg or 200kg/drum

Sinomer® UVU 62501-3D

aliphatic urethane dimethacrylate, UV oligomer, dental 3D printing resin, low shrinkage oligomer

SINOMER® UVU62501-3D is an aliphatic urethane dimethacrylate oligomer manufactured for dental 3D printing, optical coatings, and UV adhesives. As an ISO certified supplier, we provide this flexible, low-shrinkage oligomer with excellent adhesion to plastics and metals, anti-yellowing, and hydrolysis resistance.

产品描述 :

Aliphatic Urethane Dimethacrylate
Viscosity (60℃) :

5,000 – 15,000mPa·s
Functionality :

2
Color (fe/co) :

0
包装规格 :

20kg or 200kg/drum

Sinomer® UVU 62001SP-3D

urethane methacrylate, UV oligomer, Sartomer CN1970 alternative, dental model resin

SINOMER® UVU62001SP-3D is an aliphatic urethane methacrylate oligomer manufactured for 3D printing dental models, high-performance coatings and adhesives.

产品描述 :

Urethane Methacrylate
Viscosity (25℃) :

5,500 – 9,500mPa·s
Functionality :

2
Color (fe/co) :

≤100#
包装规格 :

20kg or 200kg/drum

Sinomer® UVU 62501-3D

aliphatic urethane dimethacrylate, UV oligomer, dental 3D printing resin, low shrinkage oligomer

产品描述 :

Aliphatic Urethane Dimethacrylate
Viscosity (60℃) :

5,000 – 15,000mPa·s
Functionality :

2
Color (fe/co) :

0
包装规格 :

20kg or 200kg/drum

Sinomer® UVU6203-3D

3D Printing Dual-Cure Polyurethane-Polyurea Elastomer, Polyurethane Modified Acrylate, Sinomer® UV Oligomer

SINOMER UVU6203-3D is a two-component (A/B) dual-cure aliphatic polyurethane polyurea methacrylate elastomer resin for DLP/LCD 3D printing.

产品描述 :

Dual-Cure Aliphatic Polyurethane Polyurea Methacrylate Elastomer Resin
Viscosity (cps@25°C) :

2,500–3,500
Elongation at Break (%) :

400–800
Tensile Strength (MPa) :

10–30
Tear Strength (N) :

>60
Shore Hardness (A) :

65–85

Sinomer® UVU6203-3DF

Dual-Cure Aliphatic Polyurethane Polyurea Methacrylate Elastomer Resin;DLP 3D Printing;Hollow shoe sole print

SINOMER UVU6203-3DF is a two-component (Part A & Part B), dual-curable, aliphatic polyurethane polyurea methacrylate elastomer resin designed for DLP/LCD 3D printing. Used with curing agent: UVU6203CA-3DE.

产品描述 :

Aliphatic Polyurethane Polyurea Methacrylate Elastomer
Viscosity (cps@25°C) :

8000 ~ 13000
Elongation at Break (%) :

200 ~ 500
Tensile Strength (MPa) :

8 ~ 20
Tear Strength (N) :

＞60
Shore Hardness (A) :

75 ~ 85

Sinomer® UVU6203-3DK1

3D Printing Dual-Cure Polyurethane-Polyurea Elastomer, Polyurethane Modified Acrylate, Sinomer® UV Oligomer

SINOMER UVU6203-3DK1 is a two-component (A/B) dual-cure aliphatic polyurethane polyurea methacrylate elastomer resin with skin-friendly properties.

产品描述 :

DLP 3D Printing Dual-Cure Aliphatic Polyurethane Polyurea Methacrylate Elastomer Resin
Viscosity (cps@25°C) :

8,000–12,000
Elongation at Break (%) :

350–700
Tensile Strength (MPa) :

10–20
Tear Strength (N) :

>40

Sinomer® UVU6279F-3D

Difunctional Urethane Acrylate Diluted by 20% TPGDA

SINOMER® UVU6279F-3D is a difunctional urethane acrylate oligomer diluted by 20% TPGDA with - High Gloss & Flexible for 3D Printing & Optical Resins

产品描述 :

Difunctional Urethane Acrylate Diluted by 20% TPGDA
Viscosity (25℃) :

20000-40000cps
Functionality :

2
Color (fe/co) :

≤50#
包装规格 :

20kg or 200kg/drum

Sinomer® UVU6201L-3D

Aliphatic urethane acrylate resin for 3D printing

SINOMER® UVU6201L-3D is a difunctional aliphatic urethane acrylate resin for 3D printing with excellent transparency, moderate viscosity, high hardness, superior yellowing resistance, low odor, light color, and good toughness.

产品描述 :

Aliphatic urethane acrylate resin
Viscosity (25℃) :

1000-2000cps
Functionality :

2
Color (fe/co) :

≤60#
包装规格 :

20kg or 200kg/drum

Sinomer® UVU6203-3DF

Dual-Cure Aliphatic Polyurethane Polyurea Methacrylate Elastomer Resin;DLP 3D Printing;Hollow shoe sole print

产品描述 :

Aliphatic Polyurethane Polyurea Methacrylate Elastomer
Viscosity (cps@25°C) :

8000 ~ 13000
Elongation at Break (%) :

200 ~ 500
Tensile Strength (MPa) :

8 ~ 20
Tear Strength (N) :

＞60
Shore Hardness (A) :

75 ~ 85

Sinomer® UVU6203-3D

3D Printing Dual-Cure Polyurethane-Polyurea Elastomer, Polyurethane Modified Acrylate, Sinomer® UV Oligomer

SINOMER UVU6203-3D is a two-component (A/B) dual-cure aliphatic polyurethane polyurea methacrylate elastomer resin for DLP/LCD 3D printing.

产品描述 :

Dual-Cure Aliphatic Polyurethane Polyurea Methacrylate Elastomer Resin
Viscosity (cps@25°C) :

2,500–3,500
Elongation at Break (%) :

400–800
Tensile Strength (MPa) :

10–30
Tear Strength (N) :

>60
Shore Hardness (A) :

65–85

Sinomer® UVU6203-3DK1

3D Printing Dual-Cure Polyurethane-Polyurea Elastomer, Polyurethane Modified Acrylate, Sinomer® UV Oligomer

SINOMER UVU6203-3DK1 is a two-component (A/B) dual-cure aliphatic polyurethane polyurea methacrylate elastomer resin with skin-friendly properties.

产品描述 :

DLP 3D Printing Dual-Cure Aliphatic Polyurethane Polyurea Methacrylate Elastomer Resin
Viscosity (cps@25°C) :

8,000–12,000
Elongation at Break (%) :

350–700
Tensile Strength (MPa) :

10–20
Tear Strength (N) :

>40

Sinomer® UVU6279F-3D

Difunctional Urethane Acrylate Diluted by 20% TPGDA

SINOMER® UVU6279F-3D is a difunctional urethane acrylate oligomer diluted by 20% TPGDA with - High Gloss & Flexible for 3D Printing & Optical Resins

产品描述 :

Difunctional Urethane Acrylate Diluted by 20% TPGDA
Viscosity (25℃) :

20000-40000cps
Functionality :

2
Color (fe/co) :

≤50#
包装规格 :

20kg or 200kg/drum

Sinomer® UVU6201L-3D

Aliphatic urethane acrylate resin for 3D printing

产品描述 :

Aliphatic urethane acrylate resin
Viscosity (25℃) :

1000-2000cps
Functionality :

2
Color (fe/co) :

≤60#
包装规格 :

20kg or 200kg/drum