SINOMER® UVE 3410
(Phenolic (Novolac) Epoxy Acrylate Oligomer)
High temperature resistance
Excellent electrical insulation
High surface hardness
外观 | Pale yellow, viscous transparent liquid |
Color (Fe-Co) | ≤ 5 |
粘度 @ 25°C | 10,000 – 15,000 cps |
Acid Value | ≤ 2.5 mg KOH/g |
Refractive Index @ 25°C | 1.518 ± 0.005 |
密度 @ 25°C | 1.18 ± 0.02 g/ml |
Functionality | 4 |
UV etch resist inks and solder mask inks for printed circuit boards (PCB)
Vacuum plating primer for automotive lamps
Glass inks
Adhesives
| Component | Content (wt%) |
|---|---|
| SINOMER® UVE3410 | 52 |
| SINOMER TPGDA | 20 |
| PI 651(Sinocure BDK) | 4 |
| Phthalocyanine Blue | 1 |
| Talc Powder | 20 |
| Fumed SiO₂ | 2 |
| Leveling Agent | 1 |
| Defoamer | 1 |
Process Flow:
Panel screen printing → Baking (80±5°C, 20 min) → Film alignment → UV exposure → Developing (1.5% Sodium Carbonate solution) → Circuit pattern
Ink Performance:
| Property | Result |
|---|---|
| Alkali Developability | Good |
| Adhesion (Cross-cut, 3M tape) | 100/100 |
| Component | Content (wt%) |
|---|---|
| SINOMER® UVE3410 | 45 |
| SINOMER® UVE3421* | 13 |
| SINOMER DPHA | 10 |
| Phthalocyanine Blue | 1 |
| Talc Powder | 20 |
| PI 651-SINOCURE BDK | 5 |
| Leveling Agent | 1 |
| Defoamer | 1 |
Process Flow:
Panel screen printing → Baking (75°C, 20 min) → Film alignment → UV exposure → Developing (1.0% Sodium Carbonate solution)
Ink Performance:
| Property | Result |
|---|---|
| Alkali Developability | Good |
| Adhesion (Cross-cut, 3M tape) | 100/100 |
| Hardness | 5H |
| Heat Resistance (250°C, 30 min) | Pass |
Levelling agent/Defoamer *=Our brand Agesin® provides equivalent substitutes for brand additives such as BYK and TEGO,etc.
20 公斤 or 220 公斤/桶.
Store in a dry, clean, ventilated warehouse.
Avoid exposure to light and heat.
Be careful to prevent leakage, rain and sun during transportation