AgeSin® RH-A4410 NMP is a liquid 流变助剂 suitable for medium polar and 溶剂-free coating systems as well as room temperature curing resin systems. The additive produces a highly thixotropic flow behavior, improving anti-sagging and anti-settling properties. This additive can also be post-added.
AGESIN® Rheological agent/Liquid rheology additive
RH-A4410 NMP– Modified polyurea solution
Equivalent alternative to RHEOBYK 410;RHEOBYK-7410 ET
组成 | Modified polyurea solution |
外观 | Yellow to brown liquid |
密度 g/cm³ (23℃) | 1.0~1.2 |
粘度 cps (25°C) | 200-3000 |
溶剂 | N-Methylpyrrolidone |
Non-volatile content % | ≥48 |
This datasheet is intended to give typical results, not standard.Subject to COA.
AgeSin® RH-A4410 NMP is a liquid 流变助剂 suitable for medium polar and 溶剂-free coating systems as well as room temperature curing resin systems. The additive produces a highly thixotropic flow behavior, improving anti-sagging and anti-settling properties. This additive can also be post-added.
工业涂料:
After being added to the coating system under stirring, the additive will produce a three-dimensional network structure. The thixotropic flow behavior formed is very suitable for preventing sedimentation and anti-sagging performance without affecting leveling.
★Special attention: If it is used in combination with desiccants, discoloration may occur, possibly due to the formation of metal complexes. The rheological effectiveness in this case should be evaluated. At standard dosing, there is no negative effect on yellowing. In suspected systems, yellowing and higher additive dosages should be evaluated. When the additive is used in reactive and catalytic systems and contains nitrocellulose, we recommend testing the storage stability of the product.
PVC resins:
Liquid additives are used in many PVC resins to increase thixotropy, which allows faster processing of the plastisol during manufacturing, improves anti-settling and anti-sagging behavior. AgeSin® RH-A4410 minimizes floating in pigment pastes and controls coating set during baking. Increases stability of PVC foams during mechanical agitatio
AgeSin® RH-A4410NMP should be added to the coating system under moderate shear force to ensure uniform mixing and rapid dispersion. It does not require special temperature control, the additive can be added to the grinding stage, and is also suitable for post-addition to adjust 粘度. If the additive is suitable for this system, there will be a significant increase in the rheological effect, which depends on time and polarity. Rheological effects can generally be evaluated 2-4 hours after mixing. This additive is recommended for medium polar systems.
0.2%-0.5% additive dosage (as supplied) based on PVC resin to prevent sedimentation and floating color.
0.5%-1% additive dosage (as supplied) based on PVC resin to prevent sagging
● 25 公斤 /180 公斤/桶
Store in a dry, clean, ventilated warehouse.
Avoid exposure to light and high temperature.
Can be stored for 24 months in the original packaging.